Product Description
Silicon Carbide Bricks, Silicon Nitride Bonded Sic Brick / SiC brick is made of high quality synthetically made silicon carbide grains (SiC) and selected bonding components, including nitride, Si3N4.
Silicon Carbide Bricks has great features such as high thermal conductivity, high thermal shock resistance, low thermal expansion coefficient, high corrosion resistance, high bending strength, and excellent resistance to liquid aluminum erosion capability.
SiC brick is particularly ideal for application in high temperature furnaces and in waste incineration plants.
The Si3N4 SiC blocks are widely used as lining bricks of large aluminum electrolytic cell. Using nitride bonded silicon carbide products enlarges the tank capacity, improves the thermal conductivity, enables rapid cooling, and increases the tank production capacity at the same time. Alumina and cryolite of eutectic content can form on bricks' surface, which can protect the tank lining work layer, and prolong the tank's service life. Therefore, silicon nitride bonded silicon carbide bricks are widely used in the aluminum industry.
Silicon Carbide Bricks
|
Indexes |
Silicon Carbide Bricks |
||
|
Si3N4-SiC |
Si2ON2-SiC |
Sialon-SiC |
|
|
SiC % min |
72 |
72 |
72 |
|
Si3N4 % min |
25 |
20 |
25 |
|
Free Si % max |
|
0.4 |
|
|
0.2MPa RUL starting temperature °C min |
1750 |
1650 |
1750 |
|
Typical Apparent Porosity(%) |
15 |
18 |
14 |
|
Cold Crushing StrengthMPa |
150 |
150 |
150 |
|
Rupture Strength MPa(1400°C × 0.5h) min |
45 |
30 |
55 |
|
Room Temperature Rupture Strength MPamin |
50 |
30 |
45 |
|
Resistance to thermal shock (>= Times) (1100°CWater Cooled) |
40 |
40 |
40 |
Silicon Carbide Bricks (SiC)
|
BAND Properties |
SC-1 |
SC-90 |
|||
|
SPEC |
TYPICAL |
SPEC |
TYPICAL |
||
|
Apparent Porosity (%) |
≤18 |
13.5 |
≤17 |
14.0 |
|
|
Bulk Density |
≥2.55 |
2.65 |
≥2.45 |
2.60 |
|
|
Cold Crushing Strength (kg/cm2) |
≥700 |
1100 |
≥800 |
1100 |
|
|
Chemical Composition |
SiC |
≥88.0 |
90.0 |
≥90.0 |
91.7 |